This kind of products is applicable for 10KV cross-linkable semi-conductive shielding between conductors of extrusion insulation power cables and insulation layers. It is manufactured with domestic raw materials by Swiss BUSS extrusion equipment through compounding process. It has excellent mechanical properties and stable processability.
本產品適用于10KV擠包絕緣電力電纜導體與絕緣層交聯型半導電屏蔽，采用國內原輔助材料經先進的瑞士BUSS設備混煉加工而成，具有優良機械性能和加工穩定性。
 
Processing Indicator 加工工藝
Recommend to process with the PE extruder. 建議使用聚乙烯專用擠出機進行加工。

Model 牌號	Machine Barrel Temperature 機筒溫度	Molding Temperature 機頭溫度
YPJ-10 / YPB-10	70-110℃	110-118℃

 
 
Physical and Electrical Properties 物理和電氣性能

Item 試驗項目	Unit 單位	Technical requirements 技術要求
		YPJ-10	YPB-10
Relative Density 相對密度	g/cm3	≤1.13	≤1.16
Tensile Strength 拉伸強度	MPa	≥12	≥10
Elongation at Break 斷裂伸長率	%	≥180	≥200
20℃Volume Resisitivity 20℃體積電阻率	Ω·cm	≤100	≤100
Volume Resisitivity 體積電阻率90℃	Ω·cm	≤5000	≤2500
90℃Volume Resisitivity after air aging(100℃×168h)  100℃ 168小時空氣熱老化后 90℃時體積電阻率	Ω·cm	≤1000	≤500
Air Aging Test 空氣熱老化試驗	(135±2℃)×168h
Tensile Strength Variation After Aging 拉伸強度變化率	%	±30	±30
Elongation Variation After Aging 斷裂伸長變化率	%	±30	±30
Hot Set Test 熱延伸	200℃×0.2MPa×15min
Hot Elongation 負荷下伸長率	%	≤100	≤100
Permanent Deformation after Cooling 冷卻后永久變形(Set)	%	≤15	≤15
Peel Strength 剝離強度20℃	N/cm	----	10-45
Moisture Content 水分含量	ppm	≤900	≤900