Description and Application 產品描述和用途
FEJW125NY is a kind of oil-resistant irradiation cross-linkable halogen-free insulation compound with the highest working temperature at 125℃. It has excellent mechanical property, electrical property, flame retardant property and processability and especially excellent for oil resistant and soft performances. It is specially suitable for the insulaiton and jacketing which have strict elastic performance. It also can be used for other cables which have high temperature requirements.
FEJW125NY是一種輻照交聯耐油無鹵絕緣料，其具有優良的物理機械性能，電性能，阻燃性能以及加工性能，更為突出的是其具有較好的耐油性和柔軟性能，特別適用于對彈性要求較高的絕緣，護套上，也可用于其它有高溫要求的電纜上。產品最高使用溫度為125℃。
Processing Indicator 加工工藝
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低煙無鹵專用螺桿，長徑比L/D=20-25。
Model
牌號 |
Machine Barrel Temperature
機筒溫度 |
Molding Temprature
機頭溫度 |
| FEJW125NY |
130-150℃ |
145-160℃ |
Pyisical and Electrical Properties 物理及電性能指標
Item
試驗項目 |
Unit
單位 |
Specification
技術要求 |
Density
密度 |
g/cm3 |
≤1.45 |
Tensile Strength
拉伸強度 |
MPa |
≥10 |
Elongation at Break
斷裂伸長率 |
% |
≥180 |
Aging Conditions
空氣熱老化條件 |
/ |
158℃×168h |
Reserved Tensile Strength
拉伸強度保留率 |
% |
≥70 |
Reserved elongation at break
斷裂伸長率保留率 |
% |
≥70 |
Dielectric Strength
介電強度 |
MV/m |
≥20 |
Brittle Temperature With Low Temperature Impact
低溫沖擊脆化溫度 |
℃ |
-40 |
20℃Volume Resistivity
20℃體積電阻率 |
Ω. m |
≥1.0×1012 |
Oxygen Index
氧指數 |
% |
≥30 |
HCL Gas Evolution
HCL氣體發生量 |
Mg/g |
≤5.0 |
PH Value
PH值 |
/ |
≥4.3 |
Smoke Density煙密度
– No-flame Mode無焰模式
– Flame Mode有焰模式 |
Ds max |
≤350
≤150 |
Conductivity
電導率 |
ｕS/mm |
≤10 |
Toxicity Index
毒性指數 |
/ |
≤5.0 |
Hardness
硬度 |
Shore A |
92±2 |
Hot Set Test Condition
熱延伸實驗條件
200℃×0.2MPa×15min |
Hot Elongation
負荷下伸長率 |
% |
≤100 |
Set
冷卻后永久形變 |
% |
≤5 |
Oil-
Resistant Properties
耐油性能
902# 100℃×70h |
Retention of Tensile Strength
拉伸強度保留率 |
% |
≥60 |
Retention for Elongation at Break
斷裂伸長率保留率 |
% |
≥60 |
Oil Resistant Properties
耐油性能
903# 70℃×168h |
Retention of Tensile Strength
拉伸強度保留率 |
% |
≥60 |
Retention for Elongation at Break
斷裂伸長率保留率 |
% |
≥60 |
Suggested irradiation dose:12-18 mega-tera. 建議的輻照劑量為：12-18兆拉。
Attentions 注意事項：
1）The compound should be dried before using if the package is broken. Once package is open, recommend to run out within 12 hours.
原料破包需烘干后才能使用，材料一經開封，建議12小時之內用完。
2）Please ensure the screw, barrel, hopper are thoroughly cleaned before operation. Avoid bringing impurities while processing.
加工前確保螺桿、機筒、加料斗徹底清理干凈，加工過程中嚴禁帶入雜質。
3）If you need a faster extrusion. Please accelerate screw speed gradually to avoid inadequate plasticizing which may cause rough surface of the cables.
如果要快速擠出時，請慢慢逐漸加快螺桿轉速，以免塑化不良，電纜表面毛糙。