90℃熱塑性低煙無鹵阻燃護套料 TEWR960 - 低煙無鹵電纜料

您所在的位置：網站首頁 > > 產品中心 > XLPE絕緣材料 > 低煙無鹵電纜料90℃熱塑性低煙無鹵阻燃護套料 TEWR960

90℃熱塑性低煙無鹵阻燃護套料 TEWR960

90℃ Thermoplastic Low-smoke Halogen-free Flame-retardant Jacketing Compound ...

型號：0

參考價：￥

Description and Application 產品描述和用途
TEWR960 is a kind of thermoplastic low-smoke halogen-free flame-retardant jacketing compounds. It has good mechanical property, high-temperature resistant and processability, especially good irradiation-resistant and aging resistant properties. It is low-smoke and halogen-free, especially suitable for the jacketing which has strict aging property requirements. It is also suitable for the jacketing of K1, K3 nulcear power cables. According to The Arrhenius Equation, this product can reach 90℃and 60-year service life.
TEWR960是熱塑性低煙無鹵阻燃護套料，其具有優良的物理機械性能，耐高低溫性以及加工性能，更為突出的是其具有卓越的耐輻照性和耐熱老化性。產品低煙，無鹵，特別適用于對老化條件要求較高的電纜絕緣層，適用于制作K1，K3核電用電纜的內絕緣，根據阿累尼烏斯方程推斷，本產品符合90℃條件60年壽命的要求。

Processing Indicator 加工工藝
Recommend to use special screw for low-smoke halogen-free compound with L/D=20-25.
采用低煙無鹵專用螺桿，長徑比L/D=20-25。

Model 牌號	Machine Barrel Temperature 機筒溫度	Molding Temprature 機頭溫度
TEWR960	130-160℃	150-170℃

Physical and Eletrical Properties 物理及電性能指標

試驗項目		單位	技術要求
Density 密度		g/cm³	≤1.5
Tensile Strength 抗張強度		MPa	≥10.0
Elongation at Break 斷裂伸長率		%	≥250
Aging Conditions 老化條件		/	（110±2）℃×240 h
Changing rate of Tensile Strength 抗張強度變化率		％	≤±20
Changing Rate if Elongation 斷裂伸長率變化率		％	≤±20
High Temperature Pressure Test 高溫壓力試驗（80±2℃）		%	≤50
Volume Resistivity of Insulation 絕緣體積電阻率(1kV，20℃)		Ω·m	≥1×10¹²
Brittle Temperature With Low Temperature低溫脆化溫度		℃	-40
Dielectric Strength 介電強度(1kV，20℃)		kV/mm	≥18
HCL gas Evolution 鹵酸氣體含量測定		mg/g	≤5
PH Value PH值		/	≥4.3
Conductivity 電導率		μS/mm	≤10
Smoke Density 煙密度	No-flame Mode無焰	%	≤200
	Flame Mode 有焰	%	≤190
Toxicity Index 毒性指數		/	≤2.5
Oxygen Index 氧指數		%	≥30
UV-resistant Test 耐紫外線試驗		h	≥720
Material Life（90℃）材料壽命		年	≥60